Property | Unit |
Requirement |
Result |
---|---|---|---|
LengthFootnote (1) |
mm/m |
+0 to –5 |
-0.966 |
WidthFootnote (1) |
mm/m |
+0 to –5 |
-0.245 |
SquarenessFootnote (2) |
mm/m |
≤ 2 |
0.0 |
ThicknessFootnote (2) |
% |
± 6 |
–1.03 |
Property |
Unit |
Requirement |
Result |
---|---|---|---|
Transverse load at rupture |
N |
≥ 70 |
1 282 |
Tensile strength parallel to surface |
kPa |
≥ 1 000 |
1 946 |
Water absorption |
% |
≤ 7.0 |
2.2 |
Linear expansion @ 50% to 90% RH |
% |
≤ 0.5 |
0.18 |
Density |
kg/m3 |
≥265Footnote (2) |
266 |
Water vapour permeance (Dry cup) |
ng/(Pa·s·m2) |
≥ 287 |
1 480 |
Thermal resistance for 38 mm (RSI) |
(m2·°C/W) |
0.41 |
0.47 |
Property |
Units |
Average Results |
---|---|---|
Ultimate load |
kN |
14.24Footnote (1) |
Shear resistance |
kN/m |
5.83Footnote (1) |
Failure load (0.8 ultimate load) |
kN |
11.39Footnote (1) |
Deformation at 3.5 kN |
real mm |
4.5Footnote (2) |
residual mm |
1.53Footnote (2) |
|
Deformation at 7.0 kN |
real mm |
14.81Footnote (2) |
residual mm |
5.52Footnote (2) |
|
Deformation at 10.5 kN |
real mm |
35.18Footnote (2) |
residual mm |
17.11Footnote (2) |
|
Deformation at ultimate load |
mm |
106.91Footnote (2) |
Deformation at 0.8 ultimate load |
mm |
43.21Footnote (2) |