Results of Testing the Physical Properties of OSB with Rubinate FC 3390 as the Binder
Property	Unit	Requirement	Result
Modulus of rupture (MOR) - (after preconditioning)	MPa	≥ 17.2 average	46.4 average
Modulus of rupture (MOR) - (after preconditioning)	MPa	≥ 13.8 individual	35.0 individual
Modulus of elasticity (MOE) - (after preconditioning)	MPa	≥ 3 100 average	7 142 average
Modulus of elasticity (MOE) - (after preconditioning)	MPa	≥ 2 480 individual	5 775 individual
Internal bond - (after preconditioning)	MPa	≥ 0.345 average	0.557 average
Internal bond - (after preconditioning)	MPa	≥ 0.276 individual	0.488 individual
Bond durability - MOR after 2-h boil (tested when wet)	MPa	≥ 8.6 average	22.9 average
Bond durability - MOR after 2-h boil (tested when wet)	MPa	≥ 6.9 individual	9.9 individual
Bond durability - MOR after 6 cycles	MPa	≥ 8.6 average	39.3 average
Bond durability - MOR after 6 cycles	MPa	≥ 6.9 individual	33.4 individual
Thickness swell: 24-h soak	%	≤ 25 average	6.8 average
Thickness swell: 24-h soak	%	≤ 30 individual	7.6 individual
Linear expansion: oven-dry to saturated	%	≤ 0.40 average	0.17 average
Linear expansion: oven-dry to saturated	%	≤ 0.48 individual	0.21 individual
Linear expansion: 50% to 90% relative humidity (RH)	%	≤ 0.20 average	0.05 average
Linear expansion: 50% to 90% relative humidity (RH)	%	≤ 0.24 individual	0.06 individual

Results of Testing the Creep Properties of OSB with Rubinate FC 3390 as the Binder at 20°C
Property	Unit	Requirement	Result
Cumulative creep	mm	≤ 1.7 average	0.95 average
Cumulative creep	mm	≤ 2.04 individual	1.08 individual
Secondary creep	mm	≤ 0.4 average	0.14 average
Secondary creep	mm	≤ 0.48 individual	0.18 individual
Irrecoverable creep	mm	≤ 1.1 average	0.65 average
Irrecoverable creep	mm	≤ 1.32 individual	0.81 individual

Results of Testing the Creep Properties of OSB with Rubinate FC 3390 as the Binder at 30°C
Property	Unit	Requirement	Result
Cumulative creep	mm	≤ 2.2 average	0.86 average
Cumulative creep	mm	≤ 2.64 individual	0.94 individual
Secondary creep	mm	≤ 0.4 average	0.13 average
Secondary creep	mm	≤ 0.48 individual	0.15 individual
Irrecoverable creep	mm	≤ 1.5 average	0.58 average
Irrecoverable creep	mm	≤ 1.8 individual	0.67 individual

Results of Testing the Creep Properties of OSB with Rubinate FC 3390 as the Binder at 30°C+
Property	Unit	Requirement	Result
Cumulative creep	%	≤ 35 average	−10 average
Cumulative creep	%	≤ 42 individual	−13 individual
Secondary creep	%	≤ 0 average	−7 average
Secondary creep	%	≤ 0 individual	−17 individual
Irrecoverable creep	%	≤ 50 average	−11 average
Irrecoverable creep	%	≤ 60 individual	−17 individual

Results of Testing the MOR of OSB with Rubinate FC 3390 as the Binder
Property	Unit	Requirement	Result
Exposure after 2 h boil (modified)	MPa	≥ 8.6 average	43.4 average
Exposure after 2 h boil (modified)	MPa	≥ 6.9 individual	36.7 individual
Exposure after 6 cycles	MPa	≥ 8.6 average	39.3 average
Exposure after 6 cycles	MPa	≥ 6.9 individual	33.4 individual
At −20°C	MPa	≥ 17.2 average	54.4 average
At −20°C	MPa	≥ 13.8 individual	44.2 individual
After fungal exposure − Aspergillus niger vs. Teigh	MPa	≥ 13.8 average	45.5 average
After fungal exposure − Aspergillus niger vs. Teigh	MPa	≥ 11.0 individual	36.1 individual
After fungal exposure − Penicillium luteum	MPa	≥ 13.8 average	44.9 average
After fungal exposure − Penicillium luteum	MPa	≥ 11.0 individual	36.1 individual
After soaking in 1% hydrochloric acid	MPa	≥ 7.7 average	29.8 average
After soaking in 1% hydrochloric acid	MPa	≥ 6.2 individual	21.0 individual
After soaking in 1% sodium hydroxide	MPa	≥ 12.0 average	33.5 average
After soaking in 1% sodium hydroxide	MPa	≥ 9.6 individual	30.2 individual
After soaking in water	MPa	≥ 14.6 average	38.9 average
After soaking in water	MPa	≥ 11.7 individual	33.2 individual

Results of Testing the MOE of OSB with Rubinate FC 3390 as the Binder
Property	Unit	Requirement	Result
Exposure after 2-h boil (modified)	MPa	≥ 1 550 average	6 971 average
Exposure after 2-h boil (modified)	MPa	≥ 1 240 individual	5 597 individual
Exposure after 6 cycles	MPa	≥ 2 015 average	6 568 average
Exposure after 6 cycles	MPa	≥ 1 612 individual	5 458 individual
At −20°C	MPa	≥ 3 100 average	7 880 average
At −20°C	MPa	≥ 2 480 individual	6 688 individual
After fungal exposure − Aspergillus niger vs. Teigh	MPa	≥ 2 480 average	7 128 average
After fungal exposure − Aspergillus niger vs. Teigh	MPa	≥ 1 984 individual	5 785 individual
After fungal exposure − Penicillium luteum	MPa	≥ 2 480 average	7 336 average
After fungal exposure − Penicillium luteum	MPa	≥ 1 984 individual	6 433 individual
After soaking in 1% hydrochloric acid	MPa	≥ 2 480 average	7 171 average
After soaking in 1% hydrochloric acid	MPa	≥ 1 984 individual	5 914 individual
After soaking in 1% sodium hydroxide	MPa	≥ 2 325 average	5 912 average
After soaking in 1% sodium hydroxide	MPa	≥ 1 860 individual	5 045 individual
After soaking in water	MPa	≥ 2 790 average	6 909 average
After soaking in water	MPa	≥ 2 232 individual	5 972 individual

Results of Testing the Internal Bond of OSB with Rubinate FC 3390 as the Binder
Property	Unit	Requirement	Result
Exposure after 2-h boil (modified)	MPa	≥ 0.104	0.180
Exposure after 6 cycles	MPa	≥ 0.035	0.097
At −20°C	MPa	≥ 0.345	0.618
After fungal exposure − Aspergillus niger vs. Teigh	MPa	≥ 0.207	0.394
After fungal exposure − Penicillium luteum	MPa	≥ 0.207	0.311
After soaking in 1% hydrochloric acid	MPa	≥ 0.069	0.122
After soaking in 1% sodium hydroxide	MPa	≥ 0.155	0.192
After soaking in water	MPa	≥ 0.224	0.251