Content page
From [Institution name]
| Property |
Unit |
Requirement |
Result |
|---|---|---|---|
| Overall thickness |
mm |
Report value |
1.27 |
| Overall thickness with fleece backing |
mm |
Report value |
1.72 |
| Property |
Unit |
Requirement |
Result |
|---|---|---|---|
| Load strain properties (strain energy) - machine direction |
kN/m |
≥ 30 |
59 |
| Load strain properties (strain energy) - cross-machine direction |
kN/m |
≥ 30 |
53 |
| Water vapour transmission |
g/m2/d |
≤ 4.0 |
2.87 |
| Water absorption mass |
% |
≤ 3.0 |
2.0 |
| Static puncture (rating) |
- |
≥ 3 |
4 |
| Dynamic puncture (rating) |
- |
≥ 3 |
4 |
| Low temperature impact - original |
- |
8 out of 10 pass |
10 out of 10 pass |
| Low temperature impact - after weathering |
- |
8 out of 10 pass |
8 out of 10 pass |
| Low temperature flexibility - original |
- |
Material must not crack or exhibit any visible defects |
Pass |
| Low temperature flexibility - after heat aging |
- |
Material must not crack or exhibit any visible defects |
Pass |
| Low temperature flexibility - after weathering |
- |
Material must not crack or exhibit any visible defects |
Pass |
| Tensile strength - machine direction |
MPa |
Report value |
12.9 |
| Tensile strength - cross-machine direction |
MPa |
Report value |
11.4 |
| Lap joint tensile strength (original)- machine direction |
% |
Min. 70% of original membrane |
82 |
| Lap joint tensile strength (original) - cross-machine direction |
% |
Min. 70% of original membrane |
90 |
| Lap joint tensile strength – after 7 days in boiling water - machine direction |
% |
Min. 70% of original membrane |
84 |
| Lap joint tensile strength – after 7 days in boiling water cross-machine direction |
% |
Min. 70% of original membrane |
83 |
| Abrasion resistance ( original) - weight loss |
g |
≤ 0.4 |
0.761 |
| Abrasion resistance (original) - depth of wear |
mm |
≤ 0.30 |
0.21 |
| Abrasion resistance (after accelerated weathering) - weight loss |
g |
≤ 0.4 |
0.691 |
| Abrasion resistance (after accelerated weathering) - depth of wear |
mm |
≤ 0.30 |
0.19 |
| Adhesion to wood substrate - Pliobond 1746 adhesive |
N |
≥ 125 |
435 |
| Adhesion to wood substrate - Pliobond 7008 adhesive |
N |
≥ 125 |
420 |
| Adhesion to concrete substrate - Pliobond 1746 adhesive |
N |
≥ 125 |
268 |
| Adhesion to concrete substrate - Pliobond 7008 adhesive |
N |
≥ 125 |
177 |
| Slip resistance – dry condition (rating) - leather |
- |
≥ 0.50 |
0.5 |
| Slip resistance – dry condition (rating) - rubber |
- |
≥ 0.70 |
0.62 |
| Slip resistance – wet condition (rating) - leather |
- |
≥ 0.60 |
0.8 |
| Slip resistance – wet condition (rating) - rubber |
- |
≥ 0.65 |
0.68 |