Content page
From [Institution name]
| Property |
Unit |
Requirement |
Result |
|
|---|---|---|---|---|
| Compressive strength (initial) |
kPa |
150 |
269 |
|
| Dynamic impact resistance (mean failure energy) |
J |
≥ 2.45 |
2.6 |
|
| Creep resistance (residual thickness at 25 years/10°C) |
% |
≥ 50% at 25 years/10°C |
81.6 |
|
| Cold bending at -30°C |
N/A |
No visible crack |
No visible crack |
|
| Tensile strength |
at yield |
kN/m |
≥ 8 |
XD 15.1Footnote (1) |
| elongation at break |
% |
≥ 25 |
XD 34.3 |
|
|
|
Anisotropy Ratio |
|
≥ 0.5 |
1.0 |
| Heat aging for 8 weeks |
dimensional change |
% |
≤ 1 |
MD -0.8, XD -0.2 |
| weight change |
% |
≤ –0.1 |
-0.1 |
|
| residual compression strength |
% |
≥ 80 of initial |
100.2 |
|
| Resistance to alkaline environment |
appearance |
N/A |
No visible crack |
No visible crack |
| residual compression strength |
% |
≥ 80 of initial |
100.4 |
|
| bending resistance |
N/A |
No visible cracks |
No visible crack |
|
| Geotextile fabric properties |
grab tensile |
N |
≥ 500 |
MD 650, XD 713 |
| puncture resistance |
N |
≥ 100 |
236 |
|
| trapezoid tear resistance |
N |
≥ 180 |
MD 301, XD 320 |
|
| filtration opening size by hydrodynamic sieving |
µm |
≤ 180; Report value |
120 |
|
| permittivity |
s-1 |
≥ 0.5; Report value |
1.5 |
|
| UV resistance (retained strength) |
% retained |
> 50% after 500 hours |
MD 78.2, XD 88.8 |
|
| Hydraulic transmissivity (flow rate) |
m3/h∙m |
1.33 |
4.9 |
|
| Geometrical Properties |
|||
|---|---|---|---|
| Orientation of the dimples |
- |
Report value |
Diagonal |
| Number of dimples per unit area |
dimples/m2 |
Report value |
1 554 |
| Overall thickness |
mm |
Report value |
8.67 |
| Sheet thickness |
mm |
Report value |
0.51 |
| Hollow core thickness |
mm |
Report value |
8.16 |
| Anchorage performance anchorage efficiency |
kN/anchor |
Report value |
1.13 |