Content page
From [Institution name]
| Property |
Unit |
Requirement |
Result |
|
|---|---|---|---|---|
| Compressive strength (initial) |
kPa |
150 |
223 |
|
| Dynamic impact resistance (mean failure energy) |
J |
≥ 2.45 |
8.3 |
|
| Creep resistance (residual thickness at 25 years/10°C) |
% |
≥ 40% at 25 years/10°C |
77.5 |
|
| Cold bending at -30°C |
N/A |
No visible crack |
No visible crack |
|
| Tensile strength |
at yield |
kN/m |
≥ 8 |
XDFootnote (1) 8.1 |
| elongation at break |
% |
≥ 25 |
XD 29.8 |
|
| Anisotropy ratio |
N/A |
≥ 0.5 |
1.1 |
|
| tensile strength in print area |
% |
≥ 90% of tensile strength |
100% |
|
| Heat aging for 2 weeks |
dimensional change |
% |
≤ 1 |
MDFootnote (1) -0.6, XD -0.5 |
| weight change |
% |
≤ -0.1 |
0.0 |
|
| residual compression strength |
% |
≥ 80 of initial |
107.8 |
|
| Resistance to alkaline environment |
appearance |
N/A |
No visible crack |
No visible crack |
| residual compression strength |
% |
≥ 80 of initial |
101.5 |
|
| cold bending at -30°C |
N/A |
No visible crack |
No visible crack |
|
| Geometrical properties |
|||
|---|---|---|---|
| Orientation of the dimples |
- |
Report value |
Diagonal |
| Number of dimples per unit area |
dimples/m2 |
Report value |
1 560 |
| Overall thickness |
mm |
Report value |
8.43 |
| Sheet thickness |
mm |
Report value |
0.48 |
| Hollow core thickness |
mm |
Report value |
7.95 |
| Anchorage performance anchorage efficiency |
kN/anchor |
Report value |
0.95 |