| Property |
Unit |
Requirement |
Result |
|---|---|---|---|
| Compressive strength (initial) |
kPa |
150 |
214.2 |
| Dynamic impact resistance (mean failure energy) |
J |
≥ 2.45 |
3.2 |
| Creep resistance (residual thickness at 25 years/10°C) |
% |
≥ 40% at 25 years/10°C |
60 |
| Cold bending at -30°C |
N/A |
No visible crack |
No visible crack |
| Tensile strength at yield |
kN/m |
≥ 8 |
MDFootnote (1) 8.7, XD 8.1 |
| Tensile strength elongation at break |
% |
≥ 25 |
MD 28.8, XD 25.2 |
| Heat agingFootnote (2) dimensional change |
% |
≤ 1 |
MD -0.9, XD -0.9 |
| Heat agingFootnote (2) weight change |
% |
≤ -0.1 |
-0.2Footnote (3) |
| Heat agingFootnote (2) residual compression strength |
% |
≥ 80 of initial |
103.9 |
| Heat agingFootnote (2) creep resistance (residual thickness at 25 years/10°C) |
% |
≥ 40% at 25 years/10°C |
78 |
| Resistance to alkaline environment appearance |
N/A |
No visible crack |
No visible crack |
| Resistance to alkaline environment residual compression strength |
% |
≥ 80 of initial |
107.5 |
| Resistance to alkaline environment cold bending at -30°C |
N/A |
No cracks at room temperature |
No visible crack |
| Geometrical properties |
|||
|---|---|---|---|
| orientation of dimples |
− |
Report value |
Square MD/XD |
| number of dimples per unit area |
Dimples/m 2 |
Report value |
1 059 |
| overall thickness |
mm |
Report value |
8.11 |
| sheet thickness |
mm |
Report value |
0.68 |
| hollow core thickness |
mm |
≥ 5 |
7.62 |
| Anchorage performance |
kN/anchor |
Report value |
0.77 |