Content page
From [Institution name]
| Property |
Unit |
Requirement |
Result |
|---|---|---|---|
| Thickness |
mm |
Report value |
0.099 |
| Width |
mm |
60 ± 0.8 |
60.3 |
| Length as specified |
m |
≥ 66 ± 1% |
75.8 |
| Tensile breaking strength |
N/mm |
≥ 2.8 |
6.32 |
| Elongation |
% |
≥ 150 |
1 |
| Property |
Unit |
Requirement |
Result |
|
|---|---|---|---|---|
| Adhesion after accelerated aging - to tape backing |
N/mm |
≥ 0.150 |
1.20 |
|
| Adhesion after accelerated aging - to polyethylene Footnote (1) |
N/mm |
≥ 0.150 |
1.29 |
|
| Adhesion at 23°C - to tape backing |
N/mm |
≥ 0.150 |
0.819 |
|
|
to polyethylene |
|
|
1.105 |
| Adhesion at 23°C - to polyethylene |
N/mm |
≥ 0.150 |
||
| Adhesion after heat aging - to tape backing |
N/mm |
≥ 0.20 |
0.596 |
|
| Adhesion after heat aging - to polyethylene |
N/mm |
≥ 0.20 |
0.987 |
|
| Adhesion at −10°C |
g |
≥ 250 |
5 of 5 specimens passed |
|
| Shear strength - tape to polyethylene |
% |
Ratio of mean shear strength tape-to-polyethylene and tape- to-backing ≥ 75 |
2.20 N/mm - 56Footnote (2) |
|
| Shear strength - tape to backing |
% |
Ratio of mean shear strength tape-to-polyethylene and tape- to-backing ≥ 75 |
3.95 N/mm - 56Footnote (2) |
|
| Shear strength after solvent immersion - to tape backing |
N/mm |
≥ 1.2 |
3.26 |
|
| Shear strength after solvent immersion - to polyethylene |
N/mm |
≥ 1.2 |
1.80 |
|
| Shear strength after UV and heat aging - to tape backing |
% |
No more than 25% difference from original shear strength |
4.14 N/mm - +5 |
|
| Shear strength after UV and heat aging - to polyethylene |
% |
No more than 25% difference from original shear strength |
2.20 N/mm - 0 |
|
| Bond separation (flagging) |
mm |
< 2.0 |
Pass |
|
| Shelf life (60°C for 240 hours) - to tape backing |
N/mm |
≥ 0.15 |
0.625 |
|
| Shelf life (60°C for 240 hours) - to polyethylene |
N/mm |
≥ 0.15 |
1.21 |
|